Project #2

Name

Project #2

Test Objective

To conduct recommended corrosion test on steel and aluminum (if enough product supplied).

Witnessed

Confidential

Help Implementing

Submission Date

03/29/2006

Representatives

Robert Xavier

Substrates

Aluminum
Steel

Sample Type

Product Use

Percentages Cleaned

Weight Min

Weight Max

Approximate Size

Approximate Size ID

Weight Range ID

Shape

Rough

Hardness

Hard

Shape Type

Simple

Return Samples

Return Sample Address

Contaminants

There are no related objects.

Samples Available

Pre Clean Manufacturing Step

Post Clean Manufacturing Step

Parts Cleaned Per Week

Parts Cleaned Per Bath

Frequency

PSI

Equipments

There are no related objects.

Vendor

Cleaning Chemicals

Concentration

Cleaning Temp

Cleaning Time

Cleaning Water Type

Problems With Current Method

Purpose of Cleaning

Rinse Time

Rinse Temp

Rinse Water Type

Drying Method

No relation

Drying Time

Drying Temp

Storage Type ID

How Stored

How Long Stored

Analysis Method

No relation

Performance Test

Comments or Concerns

Summary

The Tigmar 521 had more effect on the steel coupons than on the aluminum coupons. The rate of corrosion on steel was
found to be 0.000725 mm/y as compared to 0.000024 mm/y on aluminum.

Implementation

In Progress

Technolog Transfer

Analysis Only

Yes

Part Picture

Yes

Name	Class	Section
Trial #0	Trial	3
Trial #1	Trial	3

Default object view. Click to create a custom template, Node ID: 4464, Object ID: 4463

Project #2