Project #1 / Stafford Manufacturing Co / Clients / Media

Name

Project #1

Test Objective

To provide a clean part prior to heat treating for black oxide finish

Witnessed

No

Confidential

No

Help Implementing

No

Submission Date

04/18/1996

Representatives

Bill Lancy

Substrates

Steel

Sample Type

12L14 steel

Product Use

clamp collar

Percentages Cleaned

Weight Min

Weight Max

Approximate Size

2 inches OD, 1 inch ID 1/2 inch wide

Approximate Size ID

Small

Weight Range ID

Shape

Smooth

Hardness

Soft

Shape Type

Simple

Return Samples

Yes

Return Sample Address

Tom Lucciano

Contaminants

Cutting/Tapping Fluids
Lubricating/Lapping Oils
Oil

Samples Available

No

Pre Clean Manufacturing Step

Reaming

Post Clean Manufacturing Step

heat treat

Parts Cleaned Per Week

Parts Cleaned Per Bath

Frequency

PSI

Equipments

Immersion/Soak
Media Blasting
Vapor Degreasing

Vendor

Cleaning Chemicals

Chemtrol 328

Concentration

Cleaning Temp

Cleaning Time

Cleaning Water Type

Problems With Current Method

black oxide rubs off after about 1 week.

Purpose of Cleaning

to remove oils & contaminants so we can successfully blacken parts.

Rinse Time

Rinse Temp

Rinse Water Type

Drying Method

No relation

Drying Time

Drying Temp

Storage Type ID

Used Immediately

How Stored

How Long Stored

Analysis Method

Visual

Performance Test

Comments or Concerns

Summary

The lab found one cleaner that worked as well as the clients cleaner. Oakite Inproclean 1300 was used to clean a part which was then blackened.

Implementation

No

In Progress

No

Technolog Transfer

No

Analysis Only

No

Part Picture

Yes

Name	Class	Section
Trial #0	Trial	3
Trial #1	Trial	3

Default object view. Click to create a custom template, Node ID: 4226, Object ID: 4225

Project #1