| Cleaner
|
Part
|
Observations
|
| Metalnox 6386
|
Mirror Polish Lacquer
|
Pre: Buffing compound present along edges and back Post Clean: Buffing compound observed around edges Post Dry: Appears clean, some marking which could be residual coating at top of part. Edges still have buffing compound (could also be not "blasted")
|
| Satin (Grained & Wax)
|
Pre: Crystalline deposit at center Post Clean: Crystalline substance removed; no visual damage Post Dry: Appears clean with all crystalline removed
|
| Paint Prep
|
Pre: Very similar to blasted edge parts tested previously except silver Post Clean: Appears visually clean, dried very quickly (within seconds) Post Dry: Appears clean with no visual damage
|
| Mirror Polish Brass
|
Pre: Observable coating film on front of part Post Clean: Appears clean some marking or residual coating present Post Dry: Appears clean with some markings. Markings look as though they were caused from production and not damage from cleaning.
|
| SC Aircraft & Metal
|
Mirror Polish Lacquer
|
Pre: Buffing compound along edges and back Post Clean: Some residual coating remained on front surface of substrates. White film developed after rinse step which disappeared with heating. Post Dry: Residual coating remains on parts, edges still have buffing compound (could be due to not being "blasted")
|
| Satin (Grained & Wax)
|
Pre: Crystalline deposit at center of substrate Post Clean: All crystalline substance removed, minor scratch at top of substrate most likely from tweezers Post Dry: Appears clean with a slight scratch most likely from tweezers when moving substrate
|
| Paint Prep
|
Pre: Similar to blasted edge previously tested only silver Post Clean: Appears visually clean, dried very quickly Post Dry: Appears clean with no visual damge
|
| Mirror Polish Brass
|
Pre: Coating visibly present on the front surface of the substrate Post Clean: Tweezers cause slight damage to top of substrate, no other markings. Post Dry: Some residual patches of coating, scratching at top of substrate due to tweezers.
|
Overall, Metalnox and SC Aircraft were most effective for Satin and Paint Prep parts. Some residual coatings and/or markings were observed on Lacquer and Brass Mirror Polished Parts. Parts will be sent to company to review and verify effectiveness of cleaner performance. Note that Lacquer parts had been at laboratory for an extended amount of time. The aging of the soil could have impacted overall cleaner performance.