Trial #5
The purpose of this experiment was to retest Micro 90 on aluminum coupons removing all three buffing compounds using heated ultrasonics.
2020
28
2
138
Coupon
08/03/2020
15.00
Ultrasonics
Alicia McCarthy Justin Kiander
Aluminum
Buffing/Polishing Compounds
None
Air dry
Gravimetric Visual
Three aluminum coupons were obtained for each of the three buffing compounds: red, blue, and white. A solution of Micro 90 was prepared to a concentration of 5% and heated to 120°F in an ultrasonic bath. Coupons were soiled with their respective buffing compounds and a soiled weight was obtained. Once solutions reach the proper temperature, coupons were submerged and heated ultrasonics was conducted for 15 minutes, with observations noted every 5 minutes. After 15 minutes had passed, coupons were allowed to air dry. Once dry, a clean weight was obtained. Effectiveness of Micro 90 was then determined.
For all three soils, Micro 90 at a 5% concentration in an ultrasonics bath at 120°F was able to remove the buffing compounds and any additional soils present on the aluminum coupons. The next step would be to utilize Micro 90 with other high performing cleaners to test on parts provided by the company.
No relation