Two of three supplied cleaning products were diluted with DI water to vendor recommended concentration for all purpose cleaning (32:1 and 128:1). The third product was prepared following the specified procedure - oxygenating cold tap water for about 10 minutes.
Preweighed ceramic, plastic G-10 and painted steel coupons were coated with Hucker's Soil Formulation (Jif Creamy Peanut Butter 9.2%, Salted Butter 9.2%, Arrowhead Mills stone ground wheat flour 9.2%, Egg Yolk 9.2%, Evaporated milk 13.8%, Distilled water 45.8%, Printer's ink with boiled linseed oil 0.9%, Shaws saline solution 2.7%) using a handheld swab and allowed to dry for 24 hours at room temperature. The contaminated coupons were weighed again to determine the amount of soil added.
Three coupons were placed into a Gardner Straight Line Washability unit. A Kimberly-Clark Wypal reinforced paper towel was attached to the cleaning sled and soaked with 5-7 sprays of cleaning solutions. Each coupon was sprayed 7-10 times with the same cleaning solution. The cleaning unit was run for 20 cycles (~33 seconds). At the end of the cleaning, coupons were wiped once with a dry paper towel. Final weights were recorded, efficiencies were calculated and recorded.
All three products were effective at removing the glass soap scum from the three surfaces using manual wiping. The Lotus Sanitizing System resulted in the highest efficiency, removing more than 90% of the soap film. The table lists the amount of soil added, the amount remaining after cleaning and the calculated efficiency for each coupon cleaned.
| Substrate
|
Cleaner
|
Initial wt
|
Final wt
|
% Removed
|
| Ceramic
|
Lotus
|
0.1193
|
0.0098
|
91.79
|
|
|
|
0.0842
|
0.0072
|
91.45
|
|
|
|
0.0382
|
0.0094
|
75.39
|
|
|
Pleascent
|
0.1373
|
0.0073
|
94.68
|
|
|
|
0.1250
|
0.0152
|
87.84
|
|
|
|
0.0744
|
0.0019
|
97.45
|
|
|
Compass
|
0.2517
|
0.0084
|
96.66
|
|
|
|
0.1124
|
0.0111
|
90.12
|
|
|
|
0.0937
|
0.0062
|
93.38
|
| Painted steel
|
Lotus
|
0.0760
|
0.0020
|
97.37
|
|
|
|
0.0554
|
0.0021
|
96.21
|
|
|
|
0.1530
|
0.0071
|
95.36
|
|
|
Pleascent
|
0.1350
|
0.0156
|
88.44
|
|
|
|
0.4568
|
0.0224
|
95.10
|
|
|
|
0.1672
|
0.0220
|
86.84
|
|
|
Compass
|
0.1943
|
0.0029
|
98.51
|
|
|
|
0.3781
|
0.0067
|
98.23
|
|
|
|
0.0902
|
0.0028
|
96.90
|
| Plastic
|
Lotus
|
0.0665
|
0.0061
|
90.83
|
|
|
|
0.0547
|
0.0068
|
87.57
|
|
|
|
0.1252
|
0.0048
|
96.17
|
|
|
Pleascent
|
0.1039
|
0.0041
|
96.05
|
|
|
|
0.0599
|
0.0056
|
90.65
|
|
|
|
0.0798
|
0.0046
|
94.24
|
|
|
Compass
|
0.0690
|
0.0011
|
98.41
|
|
|
|
0.0821
|
0.0044
|
94.64
|
|
|
|
0.0417
|
0.0012
|
97.12
|
| Composite tile
|
Lotus
|
0.1330
|
0.0048
|
96.39
|
|
|
|
0.0885
|
0.0135
|
84.75
|
|
|
|
0.0282
|
0.0133
|
52.84
|
|
|
Pleascent
|
0.0468
|
0.0120
|
74.36
|
|
|
|
0.2268
|
0.0135
|
94.05
|
|
|
|
0.1569
|
0.0056
|
96.43
|
|
|
Compass
|
0.1016
|
0.0153
|
84.94
|
|
|
|
1.0722
|
0.0304
|
97.16
|
|
|
|
0.1332
|
0.0219
|
83.56
|